Silane modified adhesive for industrial electronics
ZJ-940 is a single component silane modified polyether adhesive that reacts with moisture in the air during use. After curing, it has good adhesion to various substrates, including metal, plastic, and glass.
Product features
Environmentally friendly products, solvent free, environmentally friendly;
Excellent adhesion performance for various substrates with different polarity;
Good extrudability and wide temperature adaptation range;
Faster surface drying time and higher initial strength.
|
Product Name |
ZJ-940 |
|
Product type |
Silane modified polyether resin |
|
Curing method |
Moisture cure |
|
Appearance |
White, black |
|
Viscosity（23℃，10rpm，cps） |
10000±1000 |
|
Density（g/cm3） |
1.35 |
|
Surface drying time（min） |
10 |
|
24h curing depth（mm） |
2.0 |
|
Complete curing time（d） |
7 |
|
Hardness（Shore A） |
61 |
|
Tensile strength（MPa） |
3.65 |
|
Elongation at break（%） |
152 |
| Adhesive strength (glass to aluminum, MPa) |
2.35 |
|
Applicable temperature range（℃） |
-40~120 |
| High temperature resistance | 150 ℃ baking for 2 days without affecting adhesion |
|
Thermal conductivity （W/mk） |
0.3 |
|
Surface resistance（Ω） |
6.3*1013 |
| Shelf life (months) |
12 |
ZJ-940 silane modified adhesive provides 330mL hard tube
When the ZJ-940 silane modified adhesive is stored in its original packaging in a cool, dry, and ventilated place, the product has a shelf life of 12 months from the date of production.